Properties and durability of wood impregnated with high melting point polyethylene wax for outdoor use was written by Zhang, Lu;Yang, Xiaojun;Chen, Zehua;Dong, Haoran;Tan, Yongjie;Bai, Xinchun. And the article was included in Journal of Wood Chemistry and Technology in 2022.Recommanded Product: 2,2-Bis(((3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoyl)oxy)methyl)propane-1,3-diyl bis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoate) This article mentions the following:
In order to develop a new wood product suitable for outdoor applications, a high m.p. polyethylene wax was used for high-pressure impregnation treatment of wood. Properties of impregnated wood were studied. Wax in molten state was stable with low viscosity, good fluidity, and easily penetrate into the wood under high pressure. Full-cell process included vacuum (-0.06 MPa for 30 min), high-pressure impregnation (0.75 MPa for 3 h) and pressure release (30 min). Wax contents of treated lodgepole pine (Pinus contorta Douglas ex Loudon.) and eucalyptus (Eucalyptus saligna) were 0.205 g/cm3 and 0.321 g/cm3, resp. Cell gaps and cell cavities of wood were filled with polyethylene wax. Nanoindentation tests showed that longitudinal mech. properties of wood cell walls were weakened after impregnation. After a 3 h high-pressure impregnation, hardness of lodgepole pine wood cell walls was reduced by 35.1%, and the modulus of elasticity was reduced by 4.9%. Treated wood had a much lower water absorption and swelling rate than untreated wood, its weathering resistance as well as insect resistance were better. In the experiment, the researchers used many compounds, for example, 2,2-Bis(((3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoyl)oxy)methyl)propane-1,3-diyl bis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoate) (cas: 6683-19-8Recommanded Product: 2,2-Bis(((3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoyl)oxy)methyl)propane-1,3-diyl bis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoate)).
2,2-Bis(((3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoyl)oxy)methyl)propane-1,3-diyl bis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoate) (cas: 6683-19-8) belongs to esters. Carboxylic acid esters of low molecular weight are colourless, volatile liquids with pleasant odours, slightly soluble in water. Cyclic esters are called lactones, regardless of whether they are derived from an organic or inorganic acid. One example of an organic lactone is γ-valerolactone.Recommanded Product: 2,2-Bis(((3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoyl)oxy)methyl)propane-1,3-diyl bis(3-(3,5-di-tert-butyl-4-hydroxyphenyl)propanoate)
Referemce:
Ester – Wikipedia,
Ester – an overview | ScienceDirect Topics