Zou, Wenjing published the artcileImproving cure performance of Si3N4 suspension with a high refractive index resin for stereolithography-based additive manufacturing, COA of Formula: C15H20O6, the publication is Ceramics International (2022), 48(9), 12569-12577, database is CAplus.
Silicon nitride (Si3N4) slurries with high solid loading, low viscosity and good stability is difficulty prepared, due to low intrinsic surface charge and a large refractive index (RI) difference between Si3N4 powder and resin. In this paper, the curing behavior of Si3N4 slurry with different functional group and RI of resin monomer were systematically researched, and then the kind and optimum content of dispersant were investigated. Subsequently, a high solid loading Si3N4 slurry (44 vol%) with good curing behavior, low viscosity and favorable stability was successfully prepared Lastly, the dense Si3N4 ceramic parts were fabricated by the suitable Si3N4 slurry (44 vol%) via stereolithog. After debinding and sintering process, the relative d. and flexural strength of Si3N4 ceramic were 98.28% and 800 ± 27.28 Mpa, resp.
Ceramics International published new progress about 15625-89-5. 15625-89-5 belongs to esters-buliding-blocks, auxiliary class Polymerization Reagents,Crosslinkers, name is Trimethylolpropane triacrylate, and the molecular formula is C10H10O6, COA of Formula: C15H20O6.
Referemce:
https://en.wikipedia.org/wiki/Ester,
Ester – an overview | ScienceDirect Topics