Sun, Bingyan published the artcileFully cross-linked UV-induced peelable acrylic PSA prepared from a dual curable castor oil based urethane acrylate oligomer for wafer dicing, Category: esters-buliding-blocks, the publication is Progress in Organic Coatings (2022), 106680, database is CAplus.
For UV-induced peelable PSA used in the wafer dicing process, improving the peel performance can effectively increase the process reliability and the yield of subsequent packaging process. In this work, a NCO-containing castor oil-based urethane acrylate oligomer called CO-PUB with dual curable functions (UV-induced polymerization and NCO/OH reaction) was obtained by partially sealing a castor oil-based urethane oligomer with hydroxyethyl acrylate. Fourier transform IR spectroscopy (FTIR) and NMR spectrometer (NMR) results indicated that CO-PUB was successfully prepared CO-PUB, OH-containing acrylic copolymer, multifunctional acrylate monomer and photo-initiator were used to construct a UV-induced peelable adhesive for silicon wafer dicing. The results showed that NCO groups in CO-PUB underwent the NCO/OH reaction with the acrylic copolymer to obtain a vinyl pendant cross-linked acrylic copolymer. The peel strength of this peelable adhesive before UV irradiation could exceed 20 N/25 mm. After UV irradiation, the unsaturated vinyl bonds contained in it were copolymerized with the multifunctional acrylate monomer to form a fully cross-linked adhesive film and the peel strength could be reduced to below 1 N/25 mm. Compared with UV-induced peelable adhesives prepared by other reported curing agents, the adhesive prepared from CO-PUB reduced UV dose required for curing. The crosslinking degree of cured adhesive film was also increased and the gel content was up to 95%. The residual adhesive after peeling off could be reduced to about 0.32%. In addition, CO-PUB used renewable castor oil as polyol and did not need to add any organic solvent during the preparation process, providing a new idea for the green preparation of UV-induced peelable adhesive with excellent performances.
Progress in Organic Coatings published new progress about 15625-89-5. 15625-89-5 belongs to esters-buliding-blocks, auxiliary class Polymerization Reagents,Crosslinkers, name is Trimethylolpropane triacrylate, and the molecular formula is C3H8N2S, Category: esters-buliding-blocks.
Referemce:
https://en.wikipedia.org/wiki/Ester,
Ester – an overview | ScienceDirect Topics