Wen, Yueh Shan published an article in 1991, the title of the article was Fundamental study on microwave cured resin.HPLC of Formula: 1985-51-9 And the article contains the following content:
The composition, polymerization, and mech. properties, and the porosity of com. microwave cured (MC) resin, heat-cured (HA) resin, and the exptl. PMMA-MMA resins were investigated. The starting temperature for the polymerization of MC-resin was lower than that of HA-resin and its exothermic curve was the same as that of the exptl. resin with a redox catalyst. The starting temperature for the polymerization of the exptl. resins decreased with increasing the concentration of benzoyl peroxide (BPO) or by the use of the redox catalyst. The average mol. weights of the exptl. resins with BPO were lower than those of exptl. heat-curing resin, but the mol. weights increased by the use of the redox catalyst. The exptl. resins with BPO showed lower mech. strength than the exptl. heat-curing resin. However, the exptl. resins with the redox catalyst had a mech. strength equal to or higher than that of the exptl. heat-curing resin. The porosity increased with increasing the concentration of BPO, the microwave irradiation time and the thickness of cured product. However, it was suppressed by the use of the redox catalyst. Crosslinking agents of >5 weight% also suppressed the porosity. The experimental process involved the reaction of 2,2-Dimethylpropane-1,3-diyl bis(2-methylacrylate)(cas: 1985-51-9).HPLC of Formula: 1985-51-9
The Article related to methacrylate denture resin microwave crosslinking, Pharmaceuticals: Prosthetics and Medical Goods and other aspects.HPLC of Formula: 1985-51-9
Referemce:
Ester – Wikipedia,
Ester – an overview | ScienceDirect Topics